题名: Three-dimensional processing maps and microstructural evolution of a CNT-reinforced Al-Cu-Mg nanocomposite
作者: Mokdad, F.;  Chen, D. L.;  Liu, Z. Y.;  Ni, D. R.;  Xiao, B. L.;  Ma, Z. Y.
发表日期: 2017-8-15
摘要: The determination of the optimum processing window of a material at elevated temperatures is essential for metal forming. Such an "ideal" processing window could be characterized by the workability parameters of power dissipation efficiency, Ziegler's instability criteria, and the presence of favorable microstructures. The purpose of the present study is to develop three-dimensional (3D) processing maps of a 2.0 wt% carbon nanotube (CNT) reinforced 2024Al nanocomposite and to manifest continuous changes of power dissipation efficiency and flow instability domains involving key processing parameters of temperature, strain rate, and strain via isothermal compressive tests. The optimal hot working parameters of the 2024A1 base alloy and the 2.0 wt% CNT/2024A1 nanocomposite were identified to be at higher temperatures and lower strain rates, with a moderately smaller processing window for the nanocomposite due to the strengthening effect of CNTs and microstructural complexities. Instability occurred at higher strain rates and lower temperatures for both base alloy and nano composite. In the stable domain dynamic recrystallization was observed to occur, and the fraction of re-crystallized grains increased with increasing deformation temperature, along with the presence of more random textures.
刊名: ELSEVIER SCIENCE SA
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Mokdad, F.,Chen, D. L.,Liu, Z. Y.,et al. Three-dimensional Processing Maps And Microstructural Evolution Of A Cnt-reinforced Al-cu-mg Nanocomposite[J]. Elsevier Science Sa,2017,702:425-437.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Mokdad, F.]'s Articles
 [Chen, D. L.]'s Articles
 [Liu, Z. Y.]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Mokdad, F.]‘s Articles
 [Chen, D. L.]‘s Articles
 [Liu, Z. Y.]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace