Anisotropy of high temperature creep properties of a Co-base single crystal superalloy

IMR OpenIR

	Anisotropy of high temperature creep properties of a Co-base single crystal superalloy
	Lu, YZ; Xie, G; Wang, D; Zhang, SH; Zheng, W; Shen, J; Lou, LH; Zhang, J; Zhang, J (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China.
	2018-03-21
发表期刊	MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
ISSN	0921-5093
卷号	720 页码:69-74
摘要	The orientation dependence of creep properties of a Co-base single crystal superalloy at 982 degrees C/248 MPa was investigated. The orientations of specimens tested were near [001, 011] and [111]. The results showed the deformation of these specimens was all controlled by a/3 < 112 > slip and stacking faults. The specimens with orientation near [001] exhibited the best creep resistance. There were a few stacking faults with two orientations in the specimens with [001] orientation. Specimens with orientations near [111] and [011] showed shorter creep lives, and stacking faults with single orientation were observed.; The orientation dependence of creep properties of a Co-base single crystal superalloy at 982 degrees C/248 MPa was investigated. The orientations of specimens tested were near [001, 011] and [111]. The results showed the deformation of these specimens was all controlled by a/3 < 112 > slip and stacking faults. The specimens with orientation near [001] exhibited the best creep resistance. There were a few stacking faults with two orientations in the specimens with [001] orientation. Specimens with orientations near [111] and [011] showed shorter creep lives, and stacking faults with single orientation were observed.
部门归属	[lu, yuzhang ; xie, guang ; wang, dong ; zhang, shaohua ; zheng, wei ; shen, jian ; lou, langhong ; zhang, jian] chinese acad sci, inst met res, shenyang 110016, liaoning, peoples r china
关键词	Alloys Deformation Ta Ti
学科领域	Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者	National Key Research and Development Program of China [2017YFB0702904]; National Natural Science Foundation of China [51631008, 51771204, U1732131]; Scientific Research Equipment Development Project of Chinese Academy of Sciences [YZ201529]
收录类别	SCI
语种	英语
WOS记录号	WOS:000429755700007
引用统计	被引频次：15[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/79422
专题	中国科学院金属研究所
通讯作者	Zhang, J (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式 GB/T 7714	Lu, YZ,Xie, G,Wang, D,et al. Anisotropy of high temperature creep properties of a Co-base single crystal superalloy[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2018,720:69-74.
APA	Lu, YZ.,Xie, G.,Wang, D.,Zhang, SH.,Zheng, W.,...&Zhang, J .(2018).Anisotropy of high temperature creep properties of a Co-base single crystal superalloy.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,720,69-74.
MLA	Lu, YZ,et al."Anisotropy of high temperature creep properties of a Co-base single crystal superalloy".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 720(2018):69-74.