题名: Modulating work-hardening behaviors and tensile plasticity of in-situ formed ductile dendrite Ti-based bulk metallic glass composites with tailored dendrite composition
作者: Liu, DM;  Zhu, ZW;  Li, ZK;  Zhang, L;  Fu, HM;  Wang, AM;  Li, H;  Zhang, HW;  Wang, YD;  Zhang, HF
发表日期: 2018-3-15
摘要: A novel series of in-situ dendrite Ti-based bulk metallic glass composites (BMGCs) were obtained. The Mo content of the dendrites monotonically increases from nil to 10.5 at% while the dendrite volume fraction and the composition of the amorphous matrix remain nearly invariant. It was found that the mechanical behaviors varied tremendously simply by changing the Mo content. Thus, the correlation between the composition and the mechanical behaviors under tension has been determined for in-situ dendrite Ti-based BMGCs for the first time. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.

Recommended Citation:
Liu, DM,Zhu, ZW,Li, ZK,et al. Modulating Work-hardening Behaviors And Tensile Plasticity Of In-situ Formed Ductile Dendrite Ti-based Bulk Metallic Glass Composites With Tailored Dendrite Composition[J]. Scripta Materialia,2018,146:22-26.

SCI Citaion Data:
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Liu, DM]'s Articles
 [Zhu, ZW]'s Articles
 [Li, ZK]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Liu, DM]‘s Articles
 [Zhu, ZW]‘s Articles
 [Li, ZK]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to  Add to Digg  Add to Reddit 
所有评论 (0)
内 容:
Email:  *
验证码:   刷新
标 题:
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.



Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace