Effects Ti/TiAlN composite multilayer coatings on corrosion resistance of titanium alloy in solid NaCl-H2O-O-2 at 600 degrees C
Zhang, MM; Xin, L; Ding, XY; Zhu, SL; Wang, FH; Xin, L (reprint author), Chinese Acad Sci, Inst Met Res, Lab Corros & Protect, 62 Wencui Rd, Shenyang, Liaoning, Peoples R China.
2018-02-15
发表期刊JOURNAL OF ALLOYS AND COMPOUNDS
ISSN0925-8388
卷号734页码:307-317
摘要This paper investigates corrosion resistance of Ti-6Al-4V coated by Ti/TiAlN composite multilayer coatings with different Ti layer thicknesses in presence of solid NaCl, H2O and O-2 at 600 degrees C. Effects of TiAlN single layer coatings with different thicknesses on the corrosion resistance of Ti-6Al-4V were also studied for comparison. The results showed that the thick TiAlN single layer coating and the Ti/TiAlN composite multilayer coating with Ti layer thickness of 0.15 mm exhibited good corrosion resistance in the above environment, while localized accelerated corrosion of substrate occurred for thin TiAlN single layer coating and Ti/TiAlN composite multilayer coating with Ti layer thickness of 0.3 mm coated specimens. It is proposed that improvement of corrosion resistance of titanium alloy by application of TiAlN single layer coating and Ti/TiAlN composite multilayer coating is attributed to suppression of active corrosion induced by gaseous metal chloride, hydrochloric acid and chlorine in the corrosion process. Accelerated local corrosion of thin TiAlN single layer coated specimen is related to existence of intrinsic through-coating defects such as pinholes in the coating. For the Ti/TiAlN composite multilayer coating with Ti layer thickness of 0.3 mm, volume expansion caused by oxidation of Ti in sublayers to TiO2 when corrosive media diffused into along through-layer defects in top TiAlN layer led to bending and cracking of the sublayers of the composite multilayer coating and eventually accelerated local corrosion of the coating and substrate. (C) 2017 Elsevier B.V. All rights reserved.; This paper investigates corrosion resistance of Ti-6Al-4V coated by Ti/TiAlN composite multilayer coatings with different Ti layer thicknesses in presence of solid NaCl, H2O and O-2 at 600 degrees C. Effects of TiAlN single layer coatings with different thicknesses on the corrosion resistance of Ti-6Al-4V were also studied for comparison. The results showed that the thick TiAlN single layer coating and the Ti/TiAlN composite multilayer coating with Ti layer thickness of 0.15 mm exhibited good corrosion resistance in the above environment, while localized accelerated corrosion of substrate occurred for thin TiAlN single layer coating and Ti/TiAlN composite multilayer coating with Ti layer thickness of 0.3 mm coated specimens. It is proposed that improvement of corrosion resistance of titanium alloy by application of TiAlN single layer coating and Ti/TiAlN composite multilayer coating is attributed to suppression of active corrosion induced by gaseous metal chloride, hydrochloric acid and chlorine in the corrosion process. Accelerated local corrosion of thin TiAlN single layer coated specimen is related to existence of intrinsic through-coating defects such as pinholes in the coating. For the Ti/TiAlN composite multilayer coating with Ti layer thickness of 0.3 mm, volume expansion caused by oxidation of Ti in sublayers to TiO2 when corrosive media diffused into along through-layer defects in top TiAlN layer led to bending and cracking of the sublayers of the composite multilayer coating and eventually accelerated local corrosion of the coating and substrate. (C) 2017 Elsevier B.V. All rights reserved.
部门归属[zhang, mingming ; ding, xueyong] northeastern univ, sch met, 3 wenhua rd, shenyang 110819, liaoning, peoples r china ; [zhang, mingming ; xin, li ; zhu, shenglong] chinese acad sci, inst met res, lab corros & protect, 62 wencui rd, shenyang, liaoning, peoples r china ; [zhu, shenglong] northeastern univ, sch mat sci & engn, 3 wenhua rd, shenyang 110819, liaoning, peoples r china
关键词Nacl Deposit Oxidation Resistance High-temperature Ti60 Alloy Ti-6al-4v Alloy Water-vapor Behavior Tin Ti6al4v Microstructure
学科领域Chemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者National Natural Science Foundation of China [U1537107]; National Key Research and Development Program of China [2017YFB0603801]
收录类别SCI
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/79501
专题中国科学院金属研究所
通讯作者Xin, L (reprint author), Chinese Acad Sci, Inst Met Res, Lab Corros & Protect, 62 Wencui Rd, Shenyang, Liaoning, Peoples R China.
推荐引用方式
GB/T 7714
Zhang, MM,Xin, L,Ding, XY,et al. Effects Ti/TiAlN composite multilayer coatings on corrosion resistance of titanium alloy in solid NaCl-H2O-O-2 at 600 degrees C[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2018,734:307-317.
APA Zhang, MM,Xin, L,Ding, XY,Zhu, SL,Wang, FH,&Xin, L .(2018).Effects Ti/TiAlN composite multilayer coatings on corrosion resistance of titanium alloy in solid NaCl-H2O-O-2 at 600 degrees C.JOURNAL OF ALLOYS AND COMPOUNDS,734,307-317.
MLA Zhang, MM,et al."Effects Ti/TiAlN composite multilayer coatings on corrosion resistance of titanium alloy in solid NaCl-H2O-O-2 at 600 degrees C".JOURNAL OF ALLOYS AND COMPOUNDS 734(2018):307-317.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhang, MM]的文章
[Xin, L]的文章
[Ding, XY]的文章
百度学术
百度学术中相似的文章
[Zhang, MM]的文章
[Xin, L]的文章
[Ding, XY]的文章
必应学术
必应学术中相似的文章
[Zhang, MM]的文章
[Xin, L]的文章
[Ding, XY]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。