Microstructures and mechanical performance of polyelectrolyte/nanocrystalline TiO2 nanolayered composites | |
Zhang,Bin1; Tan,Hai-Feng1,2; Yan,Jia-Wei2; Zhang,Ming-Dong1; Sun,Xu-Dong1; Zhang,Guang-Ping2 | |
通讯作者 | Zhang,Bin(zhangb@atm.neu.edu.cn) ; Zhang,Guang-Ping(gpzhang@imr.ac.cn) |
2013-01-21 | |
发表期刊 | Nanoscale Research Letters
![]() |
ISSN | 1556-276X |
卷号 | 8期号:1 |
摘要 | AbstractBiological materials with hierarchically laminated structures usually exhibit a good synergy between strength and fracture toughness. Here, we show that a bio-inspired (polyelectrolyte (PE)/TiO2)4 nanolayered composite with a thickness ratio of TiO2 and amorphous PE layers of about 1.1 has been prepared successfully on Si substrates by layer-by-layer self-assembly and chemical bath deposition methods. Microstructures of the nanolayered composite were investigated by scanning electron microscopy, secondary ion mass spectroscopy, and high-resolution transmission microscopy. Mechanical performance of the composite was characterized by instrumented indentation. The composite consisting of 17.9-nm-thick nanocrystalline TiO2 and 16.4-nm-thick amorphous PE layers has a strength of about 245 MPa, which is close to that of shells, while the fracture toughness of the composite, KIC?=?1.62?±?0.30 MPa?·?m1/2, is evidently higher than that of the bulk TiO2. A possible strategy to build the composite at nanoscale for high mechanical performance was addressed. |
关键词 | Bio-inspired nanolayered composite Layer-by-layer self-assembly Chemical bath deposition Mechanical property |
DOI | 10.1186/1556-276X-8-44 |
语种 | 英语 |
WOS记录号 | BMC:10.1186/1556-276X-8-44 |
出版者 | Springer New York |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.imr.ac.cn/handle/321006/80533 |
通讯作者 | Zhang,Bin; Zhang,Guang-Ping |
作者单位 | 1.Northeastern University; Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education) 2.Chinese Academy of Sciences; Shenyang National Laboratory for Materials Science, Institute of Metal Research |
推荐引用方式 GB/T 7714 | Zhang,Bin,Tan,Hai-Feng,Yan,Jia-Wei,et al. Microstructures and mechanical performance of polyelectrolyte/nanocrystalline TiO2 nanolayered composites[J]. Nanoscale Research Letters,2013,8(1). |
APA | Zhang,Bin,Tan,Hai-Feng,Yan,Jia-Wei,Zhang,Ming-Dong,Sun,Xu-Dong,&Zhang,Guang-Ping.(2013).Microstructures and mechanical performance of polyelectrolyte/nanocrystalline TiO2 nanolayered composites.Nanoscale Research Letters,8(1). |
MLA | Zhang,Bin,et al."Microstructures and mechanical performance of polyelectrolyte/nanocrystalline TiO2 nanolayered composites".Nanoscale Research Letters 8.1(2013). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论