Superplastic deformation behavior of lamellar microstructure in a hydrogenated friction stir welded Ti-6Al-4V joint
Wu, L. H.; Jia, C. L.; Han, S. C.; Li, N.; Ni, D. R.; Xiao, B. L.; Ma, Z. Y.; Fu, M. J.; Wang, Y. Q.; Zeng, Y. S.
2019-05-30
Source PublicationJOURNAL OF ALLOYS AND COMPOUNDS
ISSN0925-8388
Volume787Pages:1320-1326
AbstractIt is rather difficult for Ti alloy welds to be superplastic formed due to their low superplasticity and high flow stress. In this study, the Ti-6Al-4V alloy after hydrogenation with 0.2 wt% hydrogen was subjected to friction stir welding (FSW). The superplastic behavior of the FSW joint was investigated. The stir zone with a fine lamellar microstructure exhibited a largest elongation of 660% at 825 degrees C and 3 x 10(-3) s(-1). Besides, the stir zone showed a similar superplasticity of close to 600% to the base material at 825 degrees C, 3 x 10(-4) -1 x 10(-3) s(-1). It is the first report on the superplasticity of FSW Ti alloy joints with hydrogenation. Compared to the FSW Ti-6Al-4V alloy joint without hydrogenation, the hydrogenated FSW joint showed superior superplastic properties, including a high elongation, less than a half flow stress and lower superplastic temperature. These superior superplastic properties were mainly attributed to the globularization of the lamellar microstructure and the high fraction of beta phase induced by the hydrogen element. This study provides an effective way to reduce the difficulty of practical superplastic forming for Ti alloy welds, although a dehydrogenation process is still needed to avoid hydrogen embrittlement. (C) 2019 Elsevier B.V. All rights reserved.
KeywordTi alloys Friction stir welding Superplasticity Hydrogenation Globularization
Indexed BySCI
Language英语
WOS IDWOS:000462592500150
PublisherELSEVIER SCIENCE SA
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/81075
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Wu, L. H.,Jia, C. L.,Han, S. C.,et al. Superplastic deformation behavior of lamellar microstructure in a hydrogenated friction stir welded Ti-6Al-4V joint[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2019,787:1320-1326.
APA Wu, L. H..,Jia, C. L..,Han, S. C..,Li, N..,Ni, D. R..,...&Zeng, Y. S..(2019).Superplastic deformation behavior of lamellar microstructure in a hydrogenated friction stir welded Ti-6Al-4V joint.JOURNAL OF ALLOYS AND COMPOUNDS,787,1320-1326.
MLA Wu, L. H.,et al."Superplastic deformation behavior of lamellar microstructure in a hydrogenated friction stir welded Ti-6Al-4V joint".JOURNAL OF ALLOYS AND COMPOUNDS 787(2019):1320-1326.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wu, L. H.]'s Articles
[Jia, C. L.]'s Articles
[Han, S. C.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wu, L. H.]'s Articles
[Jia, C. L.]'s Articles
[Han, S. C.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wu, L. H.]'s Articles
[Jia, C. L.]'s Articles
[Han, S. C.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.