Oxidation of stainless steel in vacuum and evolution of surface oxide scales during hot-compression bonding

IMR OpenIR

	Oxidation of stainless steel in vacuum and evolution of surface oxide scales during hot-compression bonding
	Xie, Bijun; Sun, Mingyue; Xu, Bin; Wang, Chunyang; Jiang, Haiyang; Li, Dianzhong; Li, Yiyi
	2019-02-01
Source Publication	CORROSION SCIENCE
ISSN	0010-938X
Volume	147 Pages:41-52
Abstract	The oxidation behaviour of austenite stainless steel in vacuum and the evolution of oxide scales during vacuum hot-compression bonding were investigated combining XPS and TEM. The results indicate that thick duplex oxide scale with outer MnFe2O4 and inner FeCr2O4 layer was formed in a low vacuum and the complex oxide scale transformed into interfacial oxides MnCr2O4 remaining at the bonding interface after hot-compression bonding at 1200 degrees C. While in a high vacuum, nanoscale-thick oxide scale with outer Fe3O4 and inner Fe- and Cr-rich layer was observed and it decomposed during the subsequent hot-compression bonding procedure, leading to a well-bonded interface.
Keyword	Stainless steel Vacuum oxidation XPS TEM Hot-compression bonding
Indexed By	SCI
Language	英语
WOS ID	WOS:000456902100005
Publisher	PERGAMON-ELSEVIER SCIENCE LTD
Citation statistics	Cited Times:1[WOS] [WOS Record] [Related Records in WOS]
Document Type	期刊论文
Identifier	http://ir.imr.ac.cn/handle/321006/81407
Collection	中国科学院金属研究所
Recommended Citation GB/T 7714	Xie, Bijun,Sun, Mingyue,Xu, Bin,et al. Oxidation of stainless steel in vacuum and evolution of surface oxide scales during hot-compression bonding[J]. CORROSION SCIENCE,2019,147:41-52.
APA	Xie, Bijun.,Sun, Mingyue.,Xu, Bin.,Wang, Chunyang.,Jiang, Haiyang.,...&Li, Yiyi.(2019).Oxidation of stainless steel in vacuum and evolution of surface oxide scales during hot-compression bonding.CORROSION SCIENCE,147,41-52.
MLA	Xie, Bijun,et al."Oxidation of stainless steel in vacuum and evolution of surface oxide scales during hot-compression bonding".CORROSION SCIENCE 147(2019):41-52.

Files in This Item:
There are no files associated with this item.

If you have any objections to this item, please fill out the form below and the administrator will contact you as soon as possible.
Content:
Email：	*
Institution:
Verification Code:	Refresh

Any comments and suggestions are welcomed.
Title:	*
Content:
Email：	*
Verification Code:	Refresh

中国科学院金属研究所机构知识库