Elastic tension induced lattice distortions in DD10 single crystal nickel-based superalloy at 500 degrees C/760 MPa using in situ neutron diffraction
Mo, Fangjie; Sun, Guangai; Yang, Zhaolong; Zhang, Changsheng; Zhang, Jian; Wang, Sucheng; Peng, Shuming
2019-01-16
Source PublicationMATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
ISSN0921-5093
Volume743Pages:504-511
AbstractA newly-developed in situ neutron diffraction method has been employed to search elastic tension induced lattice distortions in DD10 single crystal nickel-based superalloy under tensile condition of 500 degrees C/760 MPa. Multiple lattice reflections, viz., {002}, {003}, {220}, {311} were in situ measured. Two samples which were stretched along [001] direction and 18 degrees deviation of [001] direction, respectively, were measured for comparison. As samples were heated to 500 degrees C, the lattice stress of both samples gradually relaxes. With 760 MPa tension applied, the response of reflections of gamma and gamma' phases were anisotropic. Compared with 0 degrees sample, 18 degrees sample resulted in distinguishable results. Due to the large extra stress, the mismatch along [001] direction is much negative, whereas that perpendicular to [001] get slightly positive. Owing to the different stress states, gamma phase is divided into two conditions. The tetragonal distortion with c/a of gamma(perpendicular to) channel is largest, while that of gamma' phase is small. The distortions at gamma/gamma' phase boundary result in broadening the boundary of gamma' phase. In this work, a new elastic-induced lattice distortion model that enhances apprehensions to the constraint effect between gamma and gamma' phases is built, which might provide the directly experimental evidence to the origin of rafting.
KeywordSingle crystal Nickel-based superalloy Elastic strain in situ neutron diffraction Lattice distortion
Indexed BySCI
Language英语
WOS IDWOS:000456891500057
PublisherELSEVIER SCIENCE SA
Citation statistics
Cited Times:1[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/81447
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Mo, Fangjie,Sun, Guangai,Yang, Zhaolong,et al. Elastic tension induced lattice distortions in DD10 single crystal nickel-based superalloy at 500 degrees C/760 MPa using in situ neutron diffraction[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2019,743:504-511.
APA Mo, Fangjie.,Sun, Guangai.,Yang, Zhaolong.,Zhang, Changsheng.,Zhang, Jian.,...&Peng, Shuming.(2019).Elastic tension induced lattice distortions in DD10 single crystal nickel-based superalloy at 500 degrees C/760 MPa using in situ neutron diffraction.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,743,504-511.
MLA Mo, Fangjie,et al."Elastic tension induced lattice distortions in DD10 single crystal nickel-based superalloy at 500 degrees C/760 MPa using in situ neutron diffraction".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 743(2019):504-511.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Mo, Fangjie]'s Articles
[Sun, Guangai]'s Articles
[Yang, Zhaolong]'s Articles
Baidu academic
Similar articles in Baidu academic
[Mo, Fangjie]'s Articles
[Sun, Guangai]'s Articles
[Yang, Zhaolong]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Mo, Fangjie]'s Articles
[Sun, Guangai]'s Articles
[Yang, Zhaolong]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.