Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys
Wang, QM; Wu, YN; Ke, PL; Cao, HT; Gong, J; Sun, C; Wen, LS
通讯作者Wang, QM(qmwang@imr.ac.cn)
2004-09-01
发表期刊SURFACE & COATINGS TECHNOLOGY
ISSN0257-8972
卷号186期号:3页码:389-397
摘要NiCoCrAlY(SiB) coatings were deposited on the nickel base superalloys DZ125 and DSM11 by arc ion plating (AIP). The corrosion behavior of the bare alloys and the protective coatings in molten 75 wt.% Na2SO4 + 25 wt.% K2SO4 at 900degreesC in air was tested for 90 h. The results indicated that DZ125 superalloy suffered catastrophic corrosion after 5 It exposure and a thick porous oxide scale (500-600 mum) interspersed with Ni3S2 and alloy particles formed on the alloy. For the Cr-rich DSM11 alloy, a mild corrosion attack happened, but severe internal Al-rich oxidation occurred inside the alloy. With NiCoCrAlY and NiCoCrAlYSiB coatings, the hot corrosion resistance of the systems was improved due to the formation of an alpha-Al2O3 scale. The hot corrosion resistance of the coatings with additions of Si and B can be improved by promoting the growth of a dense and continuous alpha-Al2O3 layer in the initial stage and improving the adherence of the oxide scale to the coating in the subsequent hot corrosion process. The hot corrosion degradation mechanism of the NiCoCrAlYSiB coatings and the influence of the substrate materials on the behavior of the whole system were also investigated. (C) 2004 Elsevier B.V. All rights reserved.
关键词\NiCoCrAlY NiCoCrAlYSiB arc ion plating AIP hot corrosion molten sulfate
DOI10.1016/j.surfcoat.2003.12.020
收录类别SCI
语种英语
WOS研究方向Materials Science ; Physics
WOS类目Materials Science, Coatings & Films ; Physics, Applied
WOS记录号WOS:000223408400008
出版者ELSEVIER SCIENCE SA
引用统计
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/81909
通讯作者Wang, QM
作者单位Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714
Wang, QM,Wu, YN,Ke, PL,et al. Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys[J]. SURFACE & COATINGS TECHNOLOGY,2004,186(3):389-397.
APA Wang, QM.,Wu, YN.,Ke, PL.,Cao, HT.,Gong, J.,...&Wen, LS.(2004).Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys.SURFACE & COATINGS TECHNOLOGY,186(3),389-397.
MLA Wang, QM,et al."Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys".SURFACE & COATINGS TECHNOLOGY 186.3(2004):389-397.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Wang, QM]的文章
[Wu, YN]的文章
[Ke, PL]的文章
百度学术
百度学术中相似的文章
[Wang, QM]的文章
[Wu, YN]的文章
[Ke, PL]的文章
必应学术
必应学术中相似的文章
[Wang, QM]的文章
[Wu, YN]的文章
[Ke, PL]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。