Galvanic corrosion in molten salts: A discussion of the corrosion mechanism of two-phase Ni-20Cr-20/30Cu alloys in eutectic (Li,K)(2)CO3 at 650 degrees C
Zeng, CL; Li, J; Zhou, T
通讯作者Zeng, CL(clzeng@imr.ac.cn)
2005-10-01
发表期刊OXIDATION OF METALS
ISSN0030-770X
卷号64期号:3-4页码:207-218
摘要The corrosion of a Ni-20Cr and three ternary Ni-20Cr-Cu alloys containing 10, 20 and 30 wt.% Cu, respectively, in a eutectic (Li, K)(2)CO3 melt was studied at 650 degrees C under air. Ni-20Cr and Ni-20Cr-10Cu are solid-solution alloys, while both Ni-20Cr-20Cu and Ni-20Cr-30Cu are two-phase alloys composed of a Cu-depleted matrix together with a small amount of a Cu-rich phase. The results indicate that Ni-20Cr and Ni-20Cr-10Cu have similar corrosion rates, forming a scale of external NiO and inner Cr-rich oxides. The two-phase Ni-20Cr-20/30 Cu alloys corrode rapidly, producing a mixture of Ni-Cr-rich oxides and a Ni-Cu metallic phase, which may be ascribed to the accelerated corrosion of the Cu-depleted matrix coupled with the cathodic Cu-rich phase of the alloys. As compared to Ni-20Cr-30Cu, Ni-20Cr-20Cu suffers from more-severe corrosion, due to a smaller area fraction of the cathodic Cu-rich phase in the alloy. The galvanic corrosion mechanism is also discussed.
关键词ternary Ni-Cr-Cu alloys molten (Li, K)(2)CO3 galvanic corrosion two-phase structure
DOI10.1007/s11085-005-6559-3
收录类别SCI
语种英语
WOS研究方向Metallurgy & Metallurgical Engineering
WOS类目Metallurgy & Metallurgical Engineering
WOS记录号WOS:000231630300003
出版者SPRINGER/PLENUM PUBLISHERS
引用统计
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/82022
通讯作者Zeng, CL
作者单位Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714
Zeng, CL,Li, J,Zhou, T. Galvanic corrosion in molten salts: A discussion of the corrosion mechanism of two-phase Ni-20Cr-20/30Cu alloys in eutectic (Li,K)(2)CO3 at 650 degrees C[J]. OXIDATION OF METALS,2005,64(3-4):207-218.
APA Zeng, CL,Li, J,&Zhou, T.(2005).Galvanic corrosion in molten salts: A discussion of the corrosion mechanism of two-phase Ni-20Cr-20/30Cu alloys in eutectic (Li,K)(2)CO3 at 650 degrees C.OXIDATION OF METALS,64(3-4),207-218.
MLA Zeng, CL,et al."Galvanic corrosion in molten salts: A discussion of the corrosion mechanism of two-phase Ni-20Cr-20/30Cu alloys in eutectic (Li,K)(2)CO3 at 650 degrees C".OXIDATION OF METALS 64.3-4(2005):207-218.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zeng, CL]的文章
[Li, J]的文章
[Zhou, T]的文章
百度学术
百度学术中相似的文章
[Zeng, CL]的文章
[Li, J]的文章
[Zhou, T]的文章
必应学术
必应学术中相似的文章
[Zeng, CL]的文章
[Li, J]的文章
[Zhou, T]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。