Effects of surface roughness and build thickness on fatigue properties of selective laser melted Inconel 718 at 650 degrees C | |
Wan, H. Y.; Luo, Y. W.; Zhang, B.; Song, Z. M.; Wang, L. Y.; Zhou, Z. J.; Li, C. P.; Chen, G. F.; Zhang, G. P. | |
2020-08-01 | |
Source Publication | INTERNATIONAL JOURNAL OF FATIGUE
![]() |
Volume | 137 |
Abstract | Effects of the surface roughness and the build thickness on fatigue properties of selective laser melted Inconel 718 were investigated at 650 degrees C. The result indicated that fatigue strength was enhanced by similar to 50% after surface machining and polishing. The thinner un-machined specimens exhibit a longer fatigue lifetime than the thicker ones, while the opposite trend appears in the machined specimens. Finite element simulations reveal that the defect shape has more evident influence on fatigue properties than the defect depth when it is less than 200 mu m. Safety thresholds of the stress concentration factor and the defect depth are 2 and 50 mu m, respectively. |
DOI | 10.1016/j.ijfatigue.2020.105654 |
WOS ID | WOS:000534570200011 |
Citation statistics | |
Document Type | 期刊论文 |
Identifier | http://ir.imr.ac.cn/handle/321006/82672 |
Collection | 中国科学院金属研究所 |
Recommended Citation GB/T 7714 | Wan, H. Y.,Luo, Y. W.,Zhang, B.,et al. Effects of surface roughness and build thickness on fatigue properties of selective laser melted Inconel 718 at 650 degrees C[J]. INTERNATIONAL JOURNAL OF FATIGUE,2020,137. |
APA | Wan, H. Y..,Luo, Y. W..,Zhang, B..,Song, Z. M..,Wang, L. Y..,...&Zhang, G. P..(2020).Effects of surface roughness and build thickness on fatigue properties of selective laser melted Inconel 718 at 650 degrees C.INTERNATIONAL JOURNAL OF FATIGUE,137. |
MLA | Wan, H. Y.,et al."Effects of surface roughness and build thickness on fatigue properties of selective laser melted Inconel 718 at 650 degrees C".INTERNATIONAL JOURNAL OF FATIGUE 137(2020). |
Files in This Item: | There are no files associated with this item. |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment