Effect of sintering temperature in argon atmosphere on microstructure and properties of 3D printed alumina ceramic cores
Li, He; Liu, Yongsheng; Liu, Yansong; Zeng, Qingfeng; Hu, Kehui; Lu, Zhigang; Liang, Jingjing
2020-04-01
Source PublicationJOURNAL OF ADVANCED CERAMICS
Volume9Issue:2Pages:220-231
AbstractAlumina ceramics with different sintering temperatures in argon atmosphere were obtained using stereolithography-based 3D printing. The effects of sintering temperature on microstructure and physical and mechanical properties were investigated. The results show that the average particle size, shrinkage, bulk density, crystallite size, flexural strength, Vickers hardness, and nanoindentation hardness increased with the increase in sintering temperature, whereas the open porosity decreased with increasing sintering temperature. No change was observed in phase composition, chemical bond, atomic ratio, and surface roughness. For the sintered samples, the shrinkage in Z direction is much greater than that in X or Y direction. The optimum sintering temperature in argon atmosphere is 1350 degrees C with a shrinkage of 3.0%, 3.2%, and 5.5% in X, Y, and Z directions, respectively, flexural strength of 26.7 MPa, Vickers hardness of 198.5 HV, nanoindentation hardness of 33.1 GPa, bulk density of 2.5 g/cm3, and open porosity of 33.8%. The optimum sintering temperature was 70 degrees C higher than that sintering in air atmosphere when achieved the similar properties.
DOI10.1007/s40145-020-0362-0
WOS IDWOS:000524317400009
Citation statistics
Cited Times:5[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/82978
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Li, He,Liu, Yongsheng,Liu, Yansong,et al. Effect of sintering temperature in argon atmosphere on microstructure and properties of 3D printed alumina ceramic cores[J]. JOURNAL OF ADVANCED CERAMICS,2020,9(2):220-231.
APA Li, He.,Liu, Yongsheng.,Liu, Yansong.,Zeng, Qingfeng.,Hu, Kehui.,...&Liang, Jingjing.(2020).Effect of sintering temperature in argon atmosphere on microstructure and properties of 3D printed alumina ceramic cores.JOURNAL OF ADVANCED CERAMICS,9(2),220-231.
MLA Li, He,et al."Effect of sintering temperature in argon atmosphere on microstructure and properties of 3D printed alumina ceramic cores".JOURNAL OF ADVANCED CERAMICS 9.2(2020):220-231.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li, He]'s Articles
[Liu, Yongsheng]'s Articles
[Liu, Yansong]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li, He]'s Articles
[Liu, Yongsheng]'s Articles
[Liu, Yansong]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li, He]'s Articles
[Liu, Yongsheng]'s Articles
[Liu, Yansong]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.