Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C | |
Yu, Zhongdi; Chen, Minghui; Li, Fengjie; Zhu, Shenglong; Wang, Fuhui | |
2020-04-01 | |
Source Publication | CORROSION SCIENCE
![]() |
Volume | 165 |
Abstract | The failure of 316 stainless steel under tribo-corrosion in molten zinc alloy (Zn-0.2Al, wt%) at 460 degrees C was investigated and compared with corrosion or the sole wear. In the absence of wear, intact Fe2Al5Znx layer forms and protects the steel from dramatic corrosion. Without liquid-metal corrosion, the steel suffers from plastic deformation on friction and slight adhesive wear. While for tribo-corrosion, the synergy of corrosion and wear accounts for 90 % of material loss. Firstly, corrosion generates a brittle scale and leads to embrittlement at subsurface, which accelerate wear. Secondly, wear promotes the formation of less-protective FeZn10 scale, accelerating corrosion. |
DOI | 10.1016/j.corsci.2019.108411 |
WOS ID | WOS:000518488800043 |
Citation statistics | |
Document Type | 期刊论文 |
Identifier | http://ir.imr.ac.cn/handle/321006/82994 |
Collection | 中国科学院金属研究所 |
Recommended Citation GB/T 7714 | Yu, Zhongdi,Chen, Minghui,Li, Fengjie,et al. Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C[J]. CORROSION SCIENCE,2020,165. |
APA | Yu, Zhongdi,Chen, Minghui,Li, Fengjie,Zhu, Shenglong,&Wang, Fuhui.(2020).Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C.CORROSION SCIENCE,165. |
MLA | Yu, Zhongdi,et al."Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C".CORROSION SCIENCE 165(2020). |
Files in This Item: | There are no files associated with this item. |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment