Very long life fatigue behavior of bearing steel AISI 52100

IMR OpenIR

	Very long life fatigue behavior of bearing steel AISI 52100
	Wang, QY; Zhang, H; Sriraman, MR; Li, SX
通讯作者	Wang, QY(wangqy@imr.ac.cn)
	2005
发表期刊	ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4
ISSN	1013-9826
卷号	297-300 页码:1846-1851
摘要	For many applications, the understanding of very long life fatigue in materials becomes extremely important. In this study, the fatigue behavior of bearing steel GCr15 (conforming to AISI 52100) at very high number of cycles has been examined. Experiments on hourglass specimens were conducted in air at room temperature, for fully reversed loading condition (R=-1), using a piezoelectric fatigue testing machine operating at a frequency of 20kHz. The results indicate that the S-N data does not reach a horizontal asymptote (signifying the fatigue limit) at 107 cycles, as conventionally believed, and that the material can fracture up to 109 cycles. Therefore, to quote a fatigue limit at 107 cycles may not hold good for the material studied. The influence of defects (such as inclusions) on the crack initiation and fracture was analyzed by scanning electron microscopy.
关键词	very long life fatigue S-N data fatigue limit gigacycle fatigue subsurface crack initiation inclusion
收录类别	SCI
语种	英语
WOS研究方向	Materials Science ; Mechanics
WOS类目	Materials Science, Ceramics ; Materials Science, Multidisciplinary ; Mechanics ; Materials Science, Characterization & Testing ; Materials Science, Composites
WOS记录号	WOS:000233131202064
出版者	TRANS TECH PUBLICATIONS LTD
引用统计	被引频次：9[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/84288
专题	中国科学院金属研究所
通讯作者	Wang, QY
作者单位	Chinese Acad Sci, Met Res Inst, Shenyang Natl Lab Mat Sci, Shenyang, Peoples R China
推荐引用方式 GB/T 7714	Wang, QY,Zhang, H,Sriraman, MR,et al. Very long life fatigue behavior of bearing steel AISI 52100[J]. ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4,2005,297-300:1846-1851.
APA	Wang, QY,Zhang, H,Sriraman, MR,&Li, SX.(2005).Very long life fatigue behavior of bearing steel AISI 52100.ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4,297-300,1846-1851.
MLA	Wang, QY,et al."Very long life fatigue behavior of bearing steel AISI 52100".ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4 297-300(2005):1846-1851.