Deep-drawing of magnesium alloy sheets at warm temperatures
Zhang, S. H.; Zhang, K.; Xu, Y. C.; Wang, Z. T.; Xu, Y.; Wang, Z. G.
Corresponding AuthorZhang, S. H.(shzangs@imr.ac.cn)
2007-04-30
Source PublicationJOURNAL OF MATERIALS PROCESSING TECHNOLOGY
ISSN0924-0136
Volume185Issue:1-3Pages:147-151
AbstractIn magnesium alloy sheet products have been attracting more and more attention in recent years because of their application potentials as coverings of portable electrical devices and automotive panels. However, magnesium alloy sheets are usually formed at temperatures between 250 and 400 degrees C because of their poor plasticity at room temperature, which makes the tooling system quite complex and also the products cost expensive. A proper forming temperature range was determined. The effects of blank holding forces on the workpiece quality were analyzed by warm deep drawing of cups from magnesium alloy sheets. Therefore, appropriate process parameters were selected to avoid forming defects effectively. In the paper, a rigid blank holder was used to adjust blank holding forces. A special liquid lubricant PTFE was used on the tool surfaces. The conditions of process defects as flange wrinkling and ruptures were analyzed. Experiments were carried out to verify the computer simulation results. Efforts were made to optimize process parameters by analyzing the causes of defects in order to improve the Limit Drawing Ratio of magnesium alloy workpieces. Computer simulation with explicit finite element method was used to optimize the process parameters before carrying out the actual experiments. It is found that rolled magnesium alloy sheets have good deep drawing formability at a forming temperature range of 105-170 degrees C with the limit drawing ratio up to 2.6. It is also necessary to control the time of heating blanks. The formability will be reduced severely by excessive heating duration. (c) 2006 Published by Elsevier B.V.
Keywordmagnesium alloy warm deep drawing forming temperature liquid lubricant limit drawing ratio
DOI10.1016/j.jmatprotec.2006.03.150
Indexed BySCI
Language英语
WOS Research AreaEngineering ; Materials Science
WOS SubjectEngineering, Industrial ; Engineering, Manufacturing ; Materials Science, Multidisciplinary
WOS IDWOS:000245390000020
PublisherELSEVIER SCIENCE SA
Citation statistics
Cited Times:66[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/91859
Collection中国科学院金属研究所
Corresponding AuthorZhang, S. H.
Affiliation1.Chinese Acad Sci, Met Res Inst, Shenyang 110016, Peoples R China
2.Gifu Univ, Dept Mech Engn, Gifu, Japan
Recommended Citation
GB/T 7714
Zhang, S. H.,Zhang, K.,Xu, Y. C.,et al. Deep-drawing of magnesium alloy sheets at warm temperatures[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY,2007,185(1-3):147-151.
APA Zhang, S. H.,Zhang, K.,Xu, Y. C.,Wang, Z. T.,Xu, Y.,&Wang, Z. G..(2007).Deep-drawing of magnesium alloy sheets at warm temperatures.JOURNAL OF MATERIALS PROCESSING TECHNOLOGY,185(1-3),147-151.
MLA Zhang, S. H.,et al."Deep-drawing of magnesium alloy sheets at warm temperatures".JOURNAL OF MATERIALS PROCESSING TECHNOLOGY 185.1-3(2007):147-151.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, S. H.]'s Articles
[Zhang, K.]'s Articles
[Xu, Y. C.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, S. H.]'s Articles
[Zhang, K.]'s Articles
[Xu, Y. C.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, S. H.]'s Articles
[Zhang, K.]'s Articles
[Xu, Y. C.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.