	In Situ Reaction Synthesis and Mechanical Properties of V2AlC
	Hu, Chunfeng 1,2; He, Lingfeng 1,2; Liu, Mingyue 1; Wang, Xiaohui 1; Wang, Jingyang 1; Li, Meishuan 1; Bao, Yiwang 1; Zhou, Yanchun 1
通讯作者	Zhou, Yanchun(yczhou@imr.ac.cn)
	2008-12-01
发表期刊	JOURNAL OF THE AMERICAN CERAMIC SOCIETY
ISSN	0002-7820
卷号	91 期号:12 页码:4029-4035
摘要	A dense V2AlC ceramic was synthesized by an in situ reaction/hot pressing method using V, Al, and C powders as starting materials. The reaction path was investigated. It was found that V2AlC was produced by a reaction between Al8V5 and C. Single -phase V2AlC could be prepared using the optimized molar ratio of V:Al:C=2:1.2:0.9. The grain sizes of as-prepared V2AlC samples were temperature dependent. On increasing the temperature from 1400 degrees to 1700 degrees C, the mean grain size of V2AlC increased from 49 mu m in length and 19 mu m in width to 405 mu m in length and 106 mu m in width. The V2AlC sample sintered at 1500 degrees C exhibited the highest flexural strength of 289 MPa and a fracture toughness of 5.7 MPa.m(1/2), while the V2AlC sample prepared at 1400 degrees C showed the highest compressive strength of 742 MPa. The sample sintered at 1700 degrees C possessed the highest damage tolerance. Additionally, V2AlC could retain a high degree of Young's modulus up to 1200 degrees C. Below 800 degrees C, V2AlC showed excellent thermal shock resistance.
资助者	National Outstanding Young Scientist Foundation ; Nature Science Foundation of China ; High-tech Bureau of the Chinese Academy of Sciences ; French Atomic Energy Commission
DOI	10.1111/j.1551-2916.2008.02774.x
收录类别	SCI
语种	英语
资助项目	National Outstanding Young Scientist Foundation[59925208] ; National Outstanding Young Scientist Foundation[50125204] ; Nature Science Foundation of China[50232040] ; Nature Science Foundation of China[50302011] ; Nature Science Foundation of China[90403027] ; Nature Science Foundation of China[50832008] ; High-tech Bureau of the Chinese Academy of Sciences ; French Atomic Energy Commission
WOS研究方向	Materials Science
WOS类目	Materials Science, Ceramics
WOS记录号	WOS:000261714700032
出版者	WILEY-BLACKWELL
引用统计	被引频次：84[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/94074
专题	中国科学院金属研究所
通讯作者	Zhou, Yanchun
作者单位	1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China
推荐引用方式 GB/T 7714	Hu, Chunfeng,He, Lingfeng,Liu, Mingyue,et al. In Situ Reaction Synthesis and Mechanical Properties of V2AlC[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2008,91(12):4029-4035.
APA	Hu, Chunfeng.,He, Lingfeng.,Liu, Mingyue.,Wang, Xiaohui.,Wang, Jingyang.,...&Zhou, Yanchun.(2008).In Situ Reaction Synthesis and Mechanical Properties of V2AlC.JOURNAL OF THE AMERICAN CERAMIC SOCIETY,91(12),4029-4035.
MLA	Hu, Chunfeng,et al."In Situ Reaction Synthesis and Mechanical Properties of V2AlC".JOURNAL OF THE AMERICAN CERAMIC SOCIETY 91.12(2008):4029-4035.