Reactive Hot Pressing and Properties of Nb2AlC
Zhang, Wei1; Travitzky, Nahum1; Hu, Chunfeng2; Zhou, Yanchun2; Greil, Peter1
Corresponding AuthorTravitzky, Nahum(nahum.travitzky@ww.uni-erlangen.de)
2009-10-01
Source PublicationJOURNAL OF THE AMERICAN CERAMIC SOCIETY
ISSN0002-7820
Volume92Issue:10Pages:2396-2399
AbstractDense Nb2AlC ceramic was synthesized from NbC, Nb, and Al powder mixture at 1650 degrees C and a pressure of 30 MPa for 90 min using an in situ reaction/hot-pressing method. The reaction kinetics, microstructure, physical, and mechanical properties of the fabricated material were investigated. A thermal expansion coefficient of similar to 8.1 x 10(-6) K-1 was measured in the temperature range of 30 degrees-1050 degrees C. At room temperature a thermal conductivity of similar to 20 W. (m. K)(-1) and a Vickers hardness of similar to 4.5 GPa were determined. The material attained Young's modulus, four-point bending strength and fracture toughness of similar to 294 GPa, similar to 443 MPa, and similar to 5.9 MPa. m(1/2), respectively. The nanolayered grains with a mean grain size of 17 mu m contributed to the damage tolerance of this ceramic. Quenching from 600 degrees, 800 degrees, and 1000 degrees C into water at room temperature resulted in decrease in bending strength from 443 MPa for the as-synthesized Nb2AlC to 391, 156, and 149 MPa, respectively.
DOI10.1111/j.1551-2916.2009.03187.x
Indexed BySCI
Language英语
WOS Research AreaMaterials Science
WOS SubjectMaterials Science, Ceramics
WOS IDWOS:000270188300037
PublisherWILEY-BLACKWELL
Citation statistics
Cited Times:34[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/95874
Collection中国科学院金属研究所
Corresponding AuthorTravitzky, Nahum
Affiliation1.Univ Erlangen Nurnberg, Dept Mat Sci, D-91058 Erlangen, Germany
2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China
Recommended Citation
GB/T 7714
Zhang, Wei,Travitzky, Nahum,Hu, Chunfeng,et al. Reactive Hot Pressing and Properties of Nb2AlC[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2009,92(10):2396-2399.
APA Zhang, Wei,Travitzky, Nahum,Hu, Chunfeng,Zhou, Yanchun,&Greil, Peter.(2009).Reactive Hot Pressing and Properties of Nb2AlC.JOURNAL OF THE AMERICAN CERAMIC SOCIETY,92(10),2396-2399.
MLA Zhang, Wei,et al."Reactive Hot Pressing and Properties of Nb2AlC".JOURNAL OF THE AMERICAN CERAMIC SOCIETY 92.10(2009):2396-2399.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, Wei]'s Articles
[Travitzky, Nahum]'s Articles
[Hu, Chunfeng]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, Wei]'s Articles
[Travitzky, Nahum]'s Articles
[Hu, Chunfeng]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, Wei]'s Articles
[Travitzky, Nahum]'s Articles
[Hu, Chunfeng]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.